Coupling damage and reliability model of low-cycle fatigue and high energy impact based on the local stress–strain approach

Fatigue induced products generally bear fatigue loads accompanied by impact processes,which reduces their reliable life rapidly. This paper introduces a reliability assessment model based on a local stress–strain approach considering both low-cycle fatigue and high energy impact loads.Two coupling relationships between fatigue and impact are given with effects of an impact process on fatigue damage and effects of fatigue damage on impact performance. The analysis of the former modifies the fatigue parameters and the Manson–Coffin equation for fatigue life based on material theories. On the other hand, the latter proposes the coupling variables and the difference of fracture toughness caused by accumulative fatigue damage. To form an overall reliability model including both fatigue failure and impact failure, a competing risk model is developed. A case study of an actuator cylinder is given to validate this method.     

基于损伤力学的金属材料韧性断裂失效分析

金属韧性断裂是损伤累积的结果,以孔洞演化理论和细观损伤力学模型为基础,将韧性断裂机制

分为拉伸型和剪切型两种类型,提出了一个适用于不同变形路径的统一形式的韧性断裂准则。通过编写用户

材料子程序VUMAT,将韧性断裂准则嵌入到ABAQUS 有限元软件的准静态算法主程序中,模拟了航空铝合金

LY12CZ(Kt =1 和3)单向拉伸时材料损伤累积、裂纹萌生、扩展直至韧性断裂的物理全过程,并通过拉伸试验

验证了模型的有效性。韧性金属材料孔洞断裂机制研究表明,单调加载过程中宏观裂纹的形成是孔洞在夹杂

物和第二相微粒周围形核、长大直至聚合的结果。

     

气孔缺陷对TA15 钛合金氩弧焊接头疲劳性能的影响

对TA15钛合金氩弧焊接接头的组织和疲劳断裂特征进行了分析,对气孔缺陷和疲劳寿命的关系进行了定量表征.结果表明:疲劳裂纹起源于焊缝的亚表面或者内部气孔缺陷,当气孔尺寸较小时,断口会出现“鱼眼”形貌特征;应力水平较低时,气孔尺寸对疲劳寿命的影响尤为显著,在特定的应力水平下,可以通过构件中的气孔缺陷尺寸来预测其寿命,对于焊接结构疲劳寿命的预测和构件焊接质量的评定具有重要的工程意义.     

复合材料在飞机主承力结构上的应用及无损检测标准

综述了国内外飞机复合材料主承力结构、机身应用现状及航空制件质量验收标准应用概况,阐述了航空复合材料零件验收标准的制定依据和原则,以及航空复合材料无损检测验收标准的主要内容;对比并分析了国际主要航空企业的无损检测验收标准,简述了飞机复合材料主承力结构及机身无损检测标准的发展趋势。     

机载蒸发循环系统结构的稳健性研究

机载蒸发循环系统结构的疲劳寿命易受外界和内部环境的影响,导致无法满足设计要求。采用随机有限元法,参照设计变量和随机变量的变异性,建立机载蒸发循环系统结构疲劳寿命稳健性优化的数学模型;通过引入权因子α,将稳健性优化问题转化为结构疲劳寿命均值和标准差的双目标优化问题。结果表明:合理设置疲劳寿命均值和标准差的权因子,可有效降低设计变量和随机变量对变异的敏感性,进而提高机载蒸发循环系统结构疲劳寿命的稳健性。     

加温超载处理对提高30CrMnSiA钢构件裂纹扩展寿命的作用

对带裂纹的３０ＣｒＭｎＳｉＡ钢紧头等拉伸试件进行同时加温超载处理，经卸载冷却后，在裂纹端区产生残余压应力塑性场。这一处理方法起到延缓裂纹扩展、抑制起裂的效果。     

基于Tanaka-Mura模型的电子束焊接头疲劳裂纹萌生模拟

为揭示高温合金电子束焊接头的疲劳特性,对其开展了疲劳裂纹萌生数值模拟研究。考虑焊缝区微观组织特性,对Voronoi图法进行改进,建立了焊缝区包含柱状晶、细等轴晶及粗等轴晶的混合晶区微观组织模型;对ABAQUS进行二次开发,考虑晶粒随机取向,生成晶粒多滑移带模型。基于Tanaka-Mura位错滑移模型,编写了疲劳裂纹萌生算法,考虑晶界处裂纹的连接与合并,对算法进行了改进,并结合有限元计算建立了电子束焊接头疲劳裂纹萌生数值模拟方法。基于上述方法对GH4169电子束焊接头不同载荷大小的疲劳裂纹萌生进行数值模拟,分析了裂纹萌生过程及萌生寿命,并与试验结果进行对比验证;还探讨了不同热影响区晶粒尺寸对焊接接头疲劳裂纹萌生的影响规律。结果表明,电子束焊接头疲劳裂纹均萌生于热影响区,但随着载荷水平的提高,萌生位置向熔合区一侧靠近;当热影响区晶粒尺寸与母材区晶粒尺寸越接近时,接头疲劳寿命越长。     

微粒子喷丸技术研究进展

微粒子喷丸因其采用的弹丸介质尺寸小,具有强化基体表面并降低表面粗糙度的优点,已成为航空、能源动力等领域中一项重要的表面强化技术。目前对于该技术的研究仍处于对其强化机理的试验论证阶段,还未有完整的理论体系。对微粒子喷丸技术的原理和特点进行了综述,讨论了微粒子喷丸的强化机制,阐述了目前微粒子喷丸技术的研究现状及在各类材料中的应用,并指出了该技术的应用前景。研究各类参数对喷丸效果的影响将是微粒子喷丸发展的主要方向。     

Investigation on surface roughness,residual stress and fatigue property of milling in-situ TiB2/7050Al metal matrix composites

For higher efficiency and precision manufacturing, more and more attentions are focused on the surface roughness and residual stress of machined parts to obtain a good fatigue life. At present, the in-situ TiB₂/7050Al metal matrix composites are widely researched due to its attractive properties such as low density, good wear resistance and improved strength. It is of great significance to investigate the machined surface roughness, residual stress and fatigue life for higher efficiency and precision manufacturing of this new kind material. In this study, the surface roughness including two-dimensional and three-dimensional roughness, residual stress and fatigue life of milling in-situ TiB₂/7050Al metal matrix composites were analyzed. It was found from comparative investigation that the three-dimensional surface roughness would be more appropriate to represent the machined surface profile of milling particle reinforced metal matrix composites. The cutting temperature played a great role on the residual stress. However, the effect of increasing cutting force could slow down the transformation from compressive stress to tensile stress under 270 °C. An exponential relationship between three-dimensional roughness and fatigue life was established and the main fracture mechanism was brittle fracture with observation of obvious shellfish veins, river pattern veins and wave shaped veins in fracture surface.     

基于声发射的单层铝板高速撞击损伤类型识别

针对基于声发射技术的在轨航天器遭受空间碎片撞击损伤的评估问题,采用AUTODYN软件进行了弹丸超高速正撞击铝板所产生声发射波动信号的数值模拟,给出了二维模拟结果;对所得到的声发射信号进行小波重构,得到低频和高频部分的信号。通过研究低频和高频信号的峰值变化,发现第一和第二峰值幅度与撞击速度的变化具有一定的规律性,通过低频第二峰值幅度与第一峰值幅度比值将高速撞击损伤模式分为成坑、锥形穿孔和圆柱形穿孔三种类型。